1. Rapid plasticization, improve melt fluidity, and maintain a certain melt strength, have a certain demoulding property.
2. Suitable for all kinds of UPVC that need better plasticizing (including extrusion, injection molding and calendering processes).
3. Without reducing the vca, it can be better applied to the processing of CPVC products requiring higher vca (including extrusion and injection molding process).
| Property | Index | Unit |
| Appearance | White Powder | |
| Proportion | 0.3-0.5 | g/cm3 |
| Volatile Matter | ＜1.5 | % |
| Intrinsic Viscosity | 0.2-0.3 | |
| Melting Point(Initial Melting) | 160 | ℃ |
| Melting Point (Final Melting) | 180 | ℃ |
| 30 Mesh Screening | ＞99 | % |
*The values represent typical results only and are not considered as a specification.
| Name | PVC-1000 | PVC Heat Stabilizer(HTM2010) | Calcium Carbonate | PE Wax | ADX-1001 |
| Competitive/g | 100.0 | 1.5 | 1.5 | 0.8 | |
| Test Sample/g | 100.0 | 1.5 | 1.5 | 0.8 | 2.0 |
Red curve: Competitive Blue curve: Test Sample